# Compoziția chimică a oțelurilor inoxidabile destinate deformării la rece ## Extras din ISO 4954 : 1993: | **Denumirea tipului de oțel1** | **Componente chimice2 (% de masă)** | **Codul grupei de oțel3** | | | | | | | | | | | | --- | --- | --- | --- | --- | --- | --- | --- | --- | --- | --- | --- | --- | | **C** | **Si** | **Mn** | **P** | **S** | **Cr** | **Mo** | **Ni** | **Alte elemente** | | | | | | **Număr** | **Denumire** | **Conform standardului ISO 4954: 1979** | | **max.** | **max.** | **max.** | **max.** | | | | | | | **Oțel feritic** | | | | | | | | | | | | | | 71 | X 3 Cr 17 E | – | ≤0,04 | 1,00 | 1,00 | 0,04 | 0,03 | 16 – 18 | – | ≤1,0 | – | F1 | | 72 | X 6 Cr 17 E | D1 | ≤0,08 | 1,00 | 1,00 | 0,04 | 0,03 | 16 – 18 | – | ≤1,0 | – | F1 | | 73 | X 6 CrMo 17 1 E | D2 | ≤0,08 | 1,00 | 1,00 | 0,04 | 0,03 | 16 – 18 | 0,9 – 1,30 | ≤1,0 | – | F1 | | 74 | X 6 CrTi 12 E | – | ≤0,08 | 1,00 | 1,00 | 0,04 | 0,03 | 10,5 – 12,5 | – | ≤0,50 | Ti: 6 x %C≤1,0 | F1 | | 75 | X 6 CrNb 12 E | – | ≤0,08 | 1,00 | 1,00 | 0,04 | 0,03 | 10,5 – 12,5 | – | ≤0,50 | Nb: 6 x % C≤1,0 | F1 | | **Oțel martensitic** | | | | | | | | | | | | | | 76 | X 12 Cr 13 E | D10 | 0,09 – 0,15 | 1,00 | 1,00 | 0,04 | 0,03 | 11,5 – 13,5 | – | ≤1,0 | – | C1 | | 77 | X 19 CrNi 16 2 E | D12 | 0,14 – 0,23 | 1,00 | 1,00 | 0,04 | 0,03 | 15 – 17,5 | – | 1,5 – 2,5 | – | C3 | | **Oțel austenitic** | | | | | | | | | | | | | | 78 | X 2 CrNi 18 10 E | D20 | ≤0,030 | 1,00 | 2,00 | 0,045 | 0,03 | 17,0 – 19,0 | – | 9,0 – 12,0 | – | A24) | | 79 | X 5 CrNi 18 9 E | D21 | ≤0,07 | 1,00 | 2,00 | 0,045 | 0,03 | 17,0 – 19,0 | – | 8,0 – 11,0 | – | A2 | | 80 | X 10 CrNi 18 9 E | D22 | ≤0,12 | 1,00 | 2,00 | 0,045 | 0,03 | 17,0 – 19,0 | – | 8,0 – 10,0 | – | A2 | | 81 | X 5 CrNi 18 12 E | D23 | ≤0,07 | 1,00 | 2,00 | 0,045 | 0,03 | 17,0 – 19,0 | – | 11,0 – 13,0 | – | A2 | | 82 | X 6 CrNi 18 16 E | D25 | ≤0,08 | 1,00 | 2,00 | 0,045 | 0,03 | 15,0 – 17,0 | – | 17,0 – 19,0 | – | A2 | | 83 | X 6 CrNiTi 18 10 E | D26 | ≤0,08 | 1,00 | 2,00 | 0,045 | 0,03 | 17,0 – 19,0 | – | 9,0 – 12,0 | Ti: 5 x % C≤0,8 | A3 | | 84 | X 5 CrNiMo 17 12 2 E | D29 | ≤0,07 | 1,00 | 2,00 | 0,045 | 0,03 | 16,5 – 18,5 | 2,0 – 2,5 | 10,5 – 13,5 | – | A4 | | 85 | X 6 CrNiMoTi 17 12 2 E | D30 | ≤0,08 | 1,00 | 2,00 | 0,045 | 0,03 | 16,5 – 18,5 | 2,0 – 2,5 | 11,0 – 14,0 | Ti: 5 x % C≤0,8 | A5 | | 86 | X 2 CrNiMo 17 13 3 E | – | ≤0,03 | 1,00 | 2,00 | 0,045 | 0,03 | 16,5 – 18,5 | 2,5 – 3,0 | 11,5 – 14,5 | – | A44) | | 87 | X 2 CrNiMoN 17 13 3 E | – | ≤0,03 | 1,00 | 2,00 | 0,045 | 0,03 | 16,5 – 18,5 | 2,5 – 3,0 | 11,5 – 14,5 | N: 0,12- 0,22 | A44) | | 88 | X 3 CrNiCu 18 9 3 E | D32 | ≤0,04 | 1,00 | 2,00 | 0,045 | 0,03 | 17,0 – 19,0 | – | 8,5 – 10,5 | Cu:3,00-4,00 | A2 | 1. Denumirile date în prima coloană sunt numere consecutive, denumirile date în a doua coloană corespund sistemului propus în ISO/TC 17/SC 2. Denumirile din a treia coloană sunt numerele utilizate anterior din ISO 4954 : 1979 (revizuit : 1993). 2. În tabel nu sunt enumerate numeric toate elementele de aliere posibile; în măsura în care tehnologia o cere, cu acordul clientului este permisă și utilizarea altor elemente de aliere. Trebuie urmărit ca alte elemente, provenite din deșeuri sau din materia primă folosită la o altă fabricație, să nu se amestece în oțel, deoarece aceste impurități pot dăuna călibilității, proprietăților mecanice și utilizabilității. 3. Acest lucru nu este cuprins în standardul ISO 4954. 4. Rezistă excelent la coroziunea intergranulară. --- HTML: